Suspension PVDF Extrusion
Suspension PVDF Extrusion FL-2006
FL-2006 PVDF homopolymer is a fluorinated semi-crystalline thermoplastic which is obtained by polymerizing vinylidene fluoride, and easily melt-processed by standard methods of extrusion.
Melt Flow Rate（g/10min）
230℃/5.0kg, ASTM D1238
Shear Rate 100 1/s, ASTM D3835
Water Absorption（%）(Time 24 hr)
ISO 62（method 1）
Elongation at Yield（%）
Elongation at Break（%）
Hardness, Shore D（Thickness2.00mm）
Crystallization Temperature（DSC peak）（℃）
1% wt. loss / in air
2. Process safety instructions
(1). This product should be processed under 260℃,toavoid producing toxic gases；
(2). PVDF has good fire resistance and smoke inhibition property, however, when meets with fire, it will release toxic hydrogen fluoride gas and fluorocarbon compounds；
(3). Operators should take good care of personal protection during the use procedure and processing.
3. Packaging and storage
(1). PVDF is sealed in plastic bag with 25kg net weight per bag and then put into drum or cardboard.
(2). It must be stored in clean, cool, dry place.